It is the product for improving durability to minimize the determinants of the service life of (design and construction) and the impact of the deterioration factors (environmental degradation) of chemical plants, steel mills, power stations, pylons and poles, cranes, steel structures in industrial complexes, and for extending the life of steel structures and for extending of commonality.
After repairing and reinforcing fragile site (including damaged area such as welding area, etc) with epoxy resin materials, prevent corrosion of steel surface including the fragile site.
*Korea Patent No. 10-1007507(A anti-corrosive composition for non-ferrous metals and iron structures and the anti-corrosive coating method using the composition)
*Mixing ratio (main component: curing agent:powder) = 3:1:8
Zinc anti-corrosive epoxy coatings are for anti-rust and based on 75μm. Quick hardening, so operational time is short. Anti-oxidation by forming a protective layer on the steel surface. As mildly alkaline, it doesn’t make steel surface oxidized ted ion or aging. Good workability. Epoxies, urethanes, fluorine can be coated over the painting.
Where to Use
Various tanks including fuel tank, etc., water and sewage, gas pipelines, steel pipe, vessels, lock gate, water gate, steel girders for bridges and railway vehicles, power equipment (inlet channel, drainage), industrial machinery
How to Store
Keep the lid closed completely at dry and room temperature be stored away from any source of moisture. Retention period: A year in sealed can
Properties
Test
|
Unit
|
Result
|
Test Method
|
Mixing Ratio
|
Base:Hardener:Power
|
3:1:8
|
Standard Specification for Highway Bridge :2005
|
Dry Paint Condition
|
-
|
No Defects
|
Standard Specification for Highway Bridge :2005
|
Condition of inside the container
|
-
|
No Defects
|
Standard Specification for Highway Bridge :2005
|
Pot life(Mixing)
|
h
|
12
|
Standard Specification for Highway Bridge :2005
|
Nonvolatile content(Base)
|
%
|
65
|
Standard Specification for Highway Bridge :2005
|
Specific Gravity(Base)
|
-
|
1.13
|
Standard Specification for Highway Bridge :2005
|
Drying Time(Dry-Through)(Mixing)
|
h
|
2
|
Standard Specification for Highway Bridge :2005
|
Metal zinc of zinc powder
|
%
|
92.9
|
Standard Specification for Highway Bridge :2005
|
All zinc of zinc powder
|
%
|
98.2
|
Standard Specification for Highway Bridge :2005
|