Hydrocarbon resin used in hot melt Road Marking Paint
Product performance
PZX-L is a thermoplastic aliphatic hydrocarbon resin which is suitable for hot melt road marking paint. It is obtained from polymerizing C5 fraction derived from the by-product of thermal cracking of naphtha, and appearance is pale yellow transparent granular solid. It can enhance the paint’s tenacity ,hardness and adhesion, and help to form a smooth surface. It will remain stable at the Four Seasons by adding additive, and have good compatibility with rosin resins.
PRODUCT SPECIFICATIONS
| Specification | Test Method | Unit | Specification Range |
| Softening Point | ASTM-E-28 | ℃ | 95-105 |
| Color | ASTM-D1544 | GC | 5 Max |
| Melt Viscosity | ASTM-D-3236 | MPa·s | 220 Max |
| Insoluble | ASTM-E-99 | Vol% | 0.1 Max |
| Acid Value | ASTM-D-974 | Mg KOH/g | 1 Max |
Application field recommended: Hot Melt Road Marking Paint
Other use: Pressure Sensitive Adhesive
The road marking paint made by PZX-L has the following characteristics: Light color Good fluidity Good wearability Filler distributed even without setting Good thermal stability Fast drying Good in weatherability, adhesion, smudge resistance Detailed product description of the road marking paint made by PZX-L hydrocarbon resin: Chemical composition: PZX-L hydrocarbon resin, EVA,PE wax, fillers materials and so on Standard: Color :standard color is yellow and white. Optional color is red, blue, green and black Density:2.01g/cm3 Compression strength:21.9MPa Softening point:109℃ Wet film thickness:1800-2000μm Dry film thickness:1800-2000μm Glass beads content:20% Dosage :theory of 5kg/square meters The surface drying time:3 min; Full dry:10 min Times: suggest 1 time Shelf life: two years，depending upon the situation if over the deadline.
Package:25kg paper bag