Physical and mechanical properties
| Property | Unit | COMPOTEX 28563 |
COMPOTEX 29052 |
COMPOTEX 42560 |
| Mass per unit area | g/m² | 285±40 | 290±40 | 425±40 |
| Type of weave | plain | |||
| Tensile strength | ||||
| warp | N/2.5cm | ≥400 | ≥1800 | ≥175 |
| weft | N/2.5cm | ≥2500 | ≥1650 | ≥3900 |
| Thickness | mm | 0.27±15% | 0.28±15% | 0.37±15% |
| Loss on ignition | % | ≤1.5 | ≤1.5 | ≤1.5 |
| Sizing agent | silane | |||
| Standard roll size | ||||
| width | cm | 22(±1.5%) | 100(+2/-1%) | 25(±1.5%) |
| length | m | ≥50 |
||
| Property | Unit | COMPOTEX 4 3014 |
COMPOTEX 60095 |
COMPOTEX 63053 |
COMPOTEX 74013 |
| Mass per unit area | g/m² | 430±50 | 600±60 | 630±40 | 740±80 |
| Type of weave | plain | ||||
| Tensile strength | |||||
| warp | Н/2.5cm | ≥1764 | ≥2500 | ≥2750 | ≥2940 |
| weft | Н/2.5cm | ≥2548 | ≥2500 | ≥2750 | ≥2940 |
| Thickness | mm | 0.35±15% | 0.58±15% | 0.55±15% | 0.60±15% |
| Loss on ignition | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
| Sizing agent | silane | ||||
| Standard roll size | |||||
| width | cm | 100(+2%/-1%) |
100(±1.5%) |
100(+2%/-1%) |
100(+2%/-1%) |
| length | m | ≥50 | |||
Typical application:
the fabrics are used as reinforcing elements in manufacture of composite materials and fiber-glass plastics to ensure strength and durability of various structures.
Composite fiberglass articles made with the use of woven roving fabrics are widely used manufacture of large-sized parts for cars, yachts, powerboats and other small size vessels, aircrafts, especially when during production it is necessary to quickly gain thickness of material at large surface of workpiece.
Advantages:
COMPOTEX woven roving fabrics ensure even distribution of bonding and impregnating agents thus making it possible to use the fabrics as reinforcing material in manufacture of composite fiber-glass goods by winding and contact molding.