| Property | Unit | E1-62P | E1-100P | E1/1-100P | E1-125P | E3-125P | E3-200P | |
| Mass per unit area | g/m² | 67±4 | 108±6 | 110±6 | 145±9 | 145±12 | 195+16 -10 |
|
| Thickness | mm | 0,062 ±0,005 |
0,100 ±0,008 |
0,100 ±0,010 |
0,125 ±0,010 |
0,125 ±0,013 |
0,200 +0,01 -0,02 |
|
| Tensile strength | warp | N/2.5 cm | 392 | 588 | 588 | 882 | 784 | 1127 |
| weft | N/2.5 cm | 294 | 588 | 588 | 882 | 784 | 1078 | |
| Loss on ignition | % | 0.8-1.6 – silane sizing agents 1.0-1.8 – paraffin emulsion |
||||||
| Width | cm | 70/90/95/107±1% | ||||||
| Regulatory documents | GOST 19907-2015 | |||||||
| Property | Unit | E3/2-200P | 7628 | 7637 | E3-400P | ||
| Mass per unit area | g/m² | 169±25 | 203±5 | 228±10 | 380±40 | ||
| Thickness | mm | 0.165±0.020 | 0.180±0.030 | 0.22±0.035 | 0.38±0.05 | ||
| Tensile strength | warp | N/5 cm | 850* | 2300 | 2300 | 1700 | |
| weft | N/5 cm | 850* | 1400 | 2100 | 2400 | ||
| Loss on ignition | % | ≤2/≤1,8 | ≤1.8 | ≤1.8 | ≤1.1 | ||
| Sizing agent | paraffin emulsion/direct | direct | |||||
| Width | cm | 100±1 | 100-200±1 | ||||
| Regulatory documents | ТU 13.20.46-032-00205009-2017 | ||||||
*for E3/2-200P fabric, tensile strength is defined in N (kgf) / 2,5sm.
Manufacture of the material with other physical and mechanical properties is accepted upon agreeing about with a consumer.
Typical application:
Manufacture of electroinsulating and clad dielectric materials, printed circuit boards, glass textolites, circuits for radio equipment and computers, coating materials for thermal insulation of pipes and tanks, roofing and other construction purposes.
These fabrics are also used in manufacture of glass-fibre reinforced plastics for various industries: manufacturing body parts for cars, yachts, motor boats, chemically resistant vessels, pipelines, protective coatings, various structures and profiles.
Advantages:
- nonflammable,
- nonburning,
- non-toxic,
- explosion-proof,
- operating temperatures ranging from -200°С to +550°С.