Features
This product is used for lead wires of various capacitors, conductors, and jumper.
LFBS
Mfg. Process : Electro plating Composition : LFBS → Fe + Cu + Sn(Sn+Bi) Application : Electrolytic capacitors ect. Plating Thickness : 12±2µ
| Physical Characteristics | LFBS(S)/LFBS(H)
|
|
Diameter(mm)
|
0.45
|
0.45
|
0.50
|
0.60
|
0.80
|
1.00
|
|
|
Tolerance(mm)
|
±0.01
|
±0.015
|
±0.015
|
±0.02
|
±0.02
|
±0.02
|
|
|
Tensile
Strength |
kg/mm2
|
44~62
|
44~62
|
44~62
|
44~62
|
34~45
|
34~45
|
|
N/mm
|
431~608
|
431~608
|
431~608
|
431~608
|
333~441
|
333~441
|
|
|
Elongation(%)
|
12~30
|
10 under
|
10 under
|
10 under
|
17~35
|
17~35
|
|
|
Bending Probation(times)
|
12 min
|
12 min
|
15 min
|
15 min
|
19 min
|
17 min
|
|
|
Conductivity(%)
|
30±3
|
30±3
|
30±3
|
30±3
|
30±3
|
30±3
|
|
|
Plating Thickness(µ)
|
12±2
|
12±2
|
12±2
|
12±2
|
12±2
|
12±2
|
|
|
Composition(%)
|
Sn
|
Remaining
|
|||||
|
Bi
|
0.3~0.9
|
||||||
TCAW
Mfg. Process : Electro plating Composition : TCAW → Cu + Sn Application : Ceramic capacitors, Conductors, Jumper Plating Thickness : 4±1µ, 3~12µ, 10±2µ
| Physical Characteristics | TCAW
|
|
Diameter(mm)
|
0.39
|
0.50
|
0.55
|
0.60
|
0.65
|
0.80
|
1.00
|
1.20
|
|
|
Tolerance(mm)
|
±0.02
|
±0.02
|
±0.02
|
±0.02
|
±0.02
|
±0.02
|
±0.02
|
±0.02
|
|
|
Tensile
Strength |
kg/mm2
|
30 max
|
30 max
|
30 max
|
30 max
|
30 max
|
30 max
|
30 max
|
28~32
|
|
N/mm
|
294
|
294
|
294
|
294
|
294
|
294
|
294
|
274~313
|
|
|
Elongation(%)
|
10 max
|
10 max
|
10 max
|
10 max
|
10 max
|
15 max
|
15 max
|
8 max
|
|
|
Bending Probation(times)
|
3 min
|
3 min
|
3 min
|
3 min
|
3 min
|
3 min
|
3 min
|
3 min
|
|
|
Plating Thickness(µ)
|
4±1
|
3~12
|
4±1
|
3~12
|
4±1
|
10±2
|
10±2
|
10±2
|
|
|
Composition(%)
|
Sn
|
100
|
|||||||